The structure and catalytic properties of PtSn catalysts supported on SUZ-4 and ZSM-5 zeolite have been studied by using various experimental techniques including XRD,nitrogen adsorption,NH3-TPD,TG,H2-TPR and TPO techniques combined with propane dehydrogenation tests.It has been shown that SUZ-4-supported PtSnNa（PtSnNa/SUZ-4） was determined to be a better catalyst for propane dehydrogenation than conventional catalysts supported on ZSM-5,owing to its higher catalytic activity and stability.Dibenzothiophene poisoning experiments were performed to investigate the detailed structures of the two supported catalysts.The characterization of the two catalysts indicates that the distribution of Pt on the porous support affects the activity.In contrast to ZSM-5-supported catalysts,Pt particles on the PtSnNa/SUZ-4 are primarily dispersed over the external surface and are not as readily deactivated by carbon deposition.This is because that the strong acid sites of the SUZ-4 zeolite evidently prevented the impregnation of the Pt precursor H_2PtCl_6 into the zeolite.In contrast,the weak acid sites of the ZSM-5 zeolite led to more of the precursor entering the zeolite tunnels,followed by transformation to highly dispersed Pt clusters during calcination.In the case of the PtSnNa/ZSM-5,the interactions between Sn oxides and the support were lessened,owing to the weaker acidity of the ZSM-5 zeolite.The dispersed Sn oxides were therefore easier to reduce to the metallic state,thus decreasing the catalytic activity for hydrocarbon dehydrogenation.
用微型催化反应装置结合X射线衍射(XRD)、H2化学吸附、NH3吸附-程序升温脱附(NH3-TPD)和H2-程序升温还原等多种物理化学手段研究了丙烷脱氢负载型Pt Sn Na/SUZ-4催化剂中Na+助剂组分的作用。结果表明,Na+组分可中和SUZ-4载体表面的强酸中心、提高催化剂的Pt金属分散度、抑制脱氢产物的裂解和积炭的生成,从而提高催化剂的丙烷脱氢选择性和反应稳定性。但是过量Na+组分的存在会削弱Sn物种与载体之间的相互作用,使其易被还原,导致催化剂丙烷脱氢活性显著下降。