Copolymer of maleic acid and acrylic acid （PMA-100）, combining with polyvinyl butyral （PVB） ultrafiltration membrane was used for the removal of Mn（II） from waste water by complexation-ultrafiltration. The carboxylic group content of PMA-100 and the rate of complexation reaction were measured. Effects of the mass ratio of PMA-100 to Mn（II） （n）, pH, background electrolyte, etc on the rejection rate （R） and permeate flux （J） were investigated. The results show that carboxylic group content of PMA-100 is 9.5 mmol/g. The complexation of Mn（II） with PMA-100 is rapid and completed within 5 min at pH 6.0. Both R and J increase with pH increasing in the range of 2.5-7.0, and R increases with the increase of n at pH 6.0 while J is little affected. The background electrolyte leads to the decrease of R, and CaCl2 has much greater effect on R than NaCl at the same ionic strength.