Superplasticity of AZ 31 magnesium matrix composites reinforced with 10 vol% SiC（2 μm） particulate i s investigated at temperature range from 365℃ to 565℃ and strain rate from 2.0 8×10-3 to 5.21×10-1 s-1. The maximum total elongation of 228 % is obtained at a strain rate of 2.08×10-1 s-1. The strain rate se nsitivity exponent （m） higher than 0.3, is observed when the strain rate is high er than 10-1 s-1 at 525℃. Increasing the test temperature to 540℃, the maximum total elongation exceeding 195% is achieved at a higher strain rate of 5.21×10-1 s-1 than that at 525℃. SiC in AZ31/SiCp composite ca n fine the matrix grain size. Filament is observed on the fracture surface of th e specimens showing superplasticity.