In this paper, the effects of rheo-diecast process parameters and T6 heat treatment on the microstructure and mechanical properties of the rheo-diecasting（RDC） semi-solid A390 alloy prepared through pure copper serpentine channel were investigated. The results indicate that the mechanical properties of the RDC samples change with the pouring temperature and injection pressure. In this case, a lower pouring temperature results in better tensile strength and elongation of the RDC A390 alloy; however, the tensile strength and elongation decrease when the pouring temperature decreases to 660°C. Higher injection pressures result in the improved mechanical properties of the RDC A390 alloy. To some extent, T6 heat treatment improves the tensile strength and ductility of the RDC A390 alloy compared to those of the non-heat treated alloy. However, when the pouring temperature and injection pressure are greater than 670°C and 70 MPa, respectively, the mechanical properties are sharply diminished.
Kunhyok RiWei-min MaoZhi-kai ZhengMyongsik KimYongho Sin
In this study, a serpentine channel pouring process was used to prepare the semi-solid A1-20%Si alloy slurry and refine primary Si grains in the alloy. The effects of the pouring temperature, number of curves in the serpentine channel, and material of the serpentine channel on the size of primary Si grains in the semi-solid A1-20%Si alloy slurry were investigated. The results showed that the pouting temperature, number of the curves, and material of the channel strongly affected the size and distribution of the primary Si grains. The pouring tempera- ture exerted the strongest effect, followed by the number of the curves and then the material of the channel. Under experimental conditions of a four-curve copper channel and a pouring temperature of 701℃, primary Si grains in the semi-solid A1-20%Si alloy slurry were refined to the greatest extent, and the lath-like grains were changed into granular grains. Moreover, the equivalent grain diameter and the average shape coefficient of primary Si grains in the satisfactory semi-solid A1-20%Si alloy slurry were 24.4 μm and 0.89, respectively. Finally, the re- finement mechanism and distribution rule of primary Si grains in the slurry prepared through the serpentine channel pouring process were analyzed and discussed.
In this paper, the serpentine channel pouring process for preparing a semi-solid A390 alloy slurry and refining the primary Si grains of the A390 alloy, was used. The effects of the pouring temperature, the cooling water flow and the number of the curves on the size of the primary Si grains in the semi-solid A390 alloy slurry were investigated. The results show that the pouring temperature, the cooling water flow and the number of the curves have a major effect on the size and the distribution of primary Si grains. Under the experimental condition of the four-curve copper channel whose cooling water flow was 500 L·h-1 and the pouring temperature was 690 oC, the primary Si grains of the semi-solid A390 alloy slurry were refined to the greatest extent and the lath-like grains were changed into granular ones. Additionally, the equivalent grain diameter and the average shape factor of the primary Si grains of the satisfactory semi-solid A390 alloy slurry are 18.6 μm and 0.8, respectively. Further, the refinement mechanism of the primary Si grains through the serpentine channel pouring process was analyzed and discussed. In summary, the primary Si nuclei could be easily precipitated due to the chilling effect of the channel inner wall, thus the primary Si grains were greatly refined. Meanwhile, the subsequent alloy melt fluid also promoted the separation of primary Si grains from the inner wall, further refining the primary Si grains.
Zhi-kai ZhengWei-min MaoBing-quan YanRui YueZhi-yong Liu
The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.
Zhi-kai ZHENGYong-jian JIWei-min MAORui YUEZhi-yong LIU
The rheo-diecasting mold filling capacity and the microstructure of the semi-solid A380 aluminum alloy slurry were investigated. The results show that the mold filling capacity was strengthened with increasing pouring temperature or increasing injection pressure. Under certain process parameters, the mold cavity was fully filled. However, the mold filling capacity decreased with increasing holding time. The mold filling capacity was improved with increasing shape factor of primary α(Al) grains; however, the solid fraction and the grain size significantly increased at the same time. In addition, the microstructures along the route of the spiral samples obviously differed. The grain size decreased gradually from the near-end to the far-end, whereas the shape factor increased gradually.
The semi-solid slurry of A380 aluminum alloy was prepared by the serpentine channel. The effects of pouring temperature, curve number and curve diameter of the serpentine channel on the microstructure of the semi-solid A380 aluminum alloy slurry were investigated. The results show that the satisfactory semi-solid A380 aluminum alloy slurry could be obtained when the pouring temperature ranged from 630 to 650 °C. Under the same conditions, increasing the curve number or reducing the curve diameter of the serpentine channel would decrease the average diameter and increase the shape factor of the primary α（Al） grains. The ＂self-stirring＂ of the alloy melt in the serpentine channel was beneficial to the ripening of the dendrites and the spheroidizing of the primary α（Al） grains.