Highly ordered mesoporous NiMoO4 material was successfully synthesized using mesoporous silica KIT-6 as hard template via vacuum nanocasting method. The structure was characterized by means of XRD, TEM, N2 adsorption-desorption, Raman and FT-IR. The mesoporous NiMoO4 with the coexistence of a-NiMoO4 and fl-NiMoO4 showed well-ordered mesoporous structure, a bimodal pore size distribution and crystalline framework. The catalytic performance of NiMoOa was investigated for oxidative dehydrogenation of propane. It is demonstrated that the mesoporous NiMoO4 catalyst with more surface active oxygen species showed better catalytic performance in oxidative dehydrogena- tion of propane in comparison with bulk NiMoO4.
通过等体积浸渍法制备了金属有机骨架材料MIL-53(Al)(MIL:Materials of Institut Lavoisier)负载纳米Pd催化剂.采用X射线衍射(XRD)、透射电子显微镜(TEM)和X射线光电子能谱(XPS)等手段对催化剂的结构进行了表征.催化剂在反应前后XRD衍射峰保持不变,说明载体MIL-53(Al)具有良好的稳定性.采用TEM对催化剂进行表征,结果表明,MIL-53(Al)的多孔晶体结构有助于形成高度分散的纳米Pd颗粒,样品2.7%(w)Pd/MIL-53中Pd颗粒的平均粒径为2.21 nm.该催化剂在CO氧化反应中表现出较高的催化活性,115°C达到完全转化.同时催化剂可循环使用,多次反应后催化活性和催化剂结构都保持稳定.
Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of these catalysts were characterized by X-Ray Diffraction （XRD）, N2 absorption-desorption, Pyridine-Fourier Transform Infrared （Py-FTIR）, Transmission Electron Microscopy （TEM）, X-Ray Fluorescence （XRF）, Scanning Electron Microscopy （SEM） and NH3- Temperature Programmed Desorption （NH3-TPD）, and the performance of these catalysts in n-dodecane hydroisomerization was evaluated in a continuous down-flow fixed bed with a stainless steel tubular reactor. The characterization results indicated that the intergrowth zeolite ZSM-22/ZSM-23 possessed the dual structure of ZSM-22 and ZSM-23, and the catalyst Pt/ZSM-22/ZSM-23 had similar pores and weak acidity to Pt/ZSM-22 and Pt/ZSM-23 catalysts. Moreover, Pt/ZSM-22/ZSM-23 catalyst showed a high selectivity in hydroisomerization of long chain n-alkanes to mono-branched isomers. The evaluation results for n-dodecane hydroisomerization indicated that the activity of Pt/ZSM-22/ZSM-23 was the lowest, while the hydroisomerization selectivity was the highest among the three catalysts. The maximum yield of i-dodecane product was 68.3% over Pt/ZSM-22/ZSM-23 at 320 ℃.