Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B(RhB) solution and gaseous formaldehyde(FAD). With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.