In order to compare with annealed Al-4%Cu alloys, the influence of solute concentration on the serrated flow is investigated by solution treatment. In this paper, some dynamic parameters, such as critical time and the ultimate tensile strength are obtained. Moreover, the change of the strain rate range for serrated flow in Al-4%Cu alloys prepared by annealing and quenching heat treatments is reported too. The difference between them is attributed to the increasing solute concentration in the bulk of the solution treated materials.
In this paper a technique based on high-speed digital photography and the digital speckle correlation (DSC) method is used for the quantitative measurement of the displacement and strain fields of various Portevin Le Chatelier (PLC) bands (types A, B, and C). The experimental results clearly show the nucleation process of a type-B band and the propagation of a type-A band. The results also reveal that there exists an elastic shrinkage deformation outside a PLC band during a large avalanche-like deformation inside the PLC band.