Reduction of Sensitivity to Sintering Temperature for Nd-Fe-B Magnets through Zr and Nb Additions被引量：1: 2009年; To reduce the sensitivity of grain growth to sintering temperature for improving property consistency of sintered Nd-Fe-B magnets, combined additions of Zr and Nb were investigated. It was found that when Zr content was increased to 0.07 at. pct, abnormal grain growth was effectively hindered even when the sintering temperature reached 1100℃. With combined additions of 0.07 at. pct Zr and 0.07 at. pct Nb, the sensitivity of grain growth to sintering temperature was greatly reduced consistency than the magnets containing no Zr and also improved. The magnets sintered at 1100℃ showed higher property Nb. In addition, the magnetic properties of magnets were also improved.; Mi Yan Xigui Cui Lianqing Yu Tianyu Ma; 关键词：CONSISTENCY

快淬Fe_(81)Ga_(19)合金薄带的相结构和磁致伸缩被引量：7: 2009年; 采用熔体快淬法制备Fe81Ga19合金薄带,研究薄带试样的相结构和磁致伸缩性能。XRD和M-TG结果表明,快淬态Fe81Ga19合金基体为Fe(Ga)无序固溶体相,并有微量非对称结构的DO3相析出,且薄带厚度方向[100]择优取向。当测量磁场垂直带面时,薄带试样沿带长方向的饱和磁致伸缩达–1830×10-6。Fe81Ga19合金薄带的巨磁致伸缩与其大的形状各向异性、熔体快淬时合金内部形成的非对称结构的DO3相及薄带厚度方向[100]择优取向相关。; 王庆伟张晶晶马天宇严密; 关键词：熔体快淬磁致伸缩

一级回火和烧结温度对掺Dy_2O_3的Nd-Fe-B磁性能影响被引量：5: 2009年; 研究了一级回火和烧结温度T对掺Dy2O3烧结钕铁硼磁体的磁性能和微观结构的影响。结果表明:一级回火和烧结温度对磁体磁性能影响显著,尤其对矫顽力Hcj的影响。当添加2%(质量分数,下同)的Dy2O3时,一级回火可以明显提高磁体的Hcj,但烧结温度影响甚微;当添加5%的Dy2O3时,随烧结温度的提高,磁体的Hcj显著提高,但是一级回火使Hcj提高不明显。这主要归因于:一是Dy2O3发生置换反应生成Nd2O3颗粒影响烧结和回火制度,二是烧结温度影响Dy原子扩散。; 崔熙贵严密马天宇罗伟涂少军; 关键词：烧结ND-FE-B 烧结温度磁性能

Tb_(0.36)Dy_(0.64)(Fe_(0.85)Co_(0.15))_(2-x)B_x合金的结构和磁致伸缩被引量：1: 2008年; 研究了Tb0.36Dy0.64(Fe0.85Co0.15)2-xBx(x=0,0.05,0.15,0.30)合金的结构、显微组织和磁致伸缩。结果表明,Tb0.36Dy0.64(Fe0.85Co0.15)2-xBx合金基体仍为MgCu2型立方结构Laves相,合金点阵常数a随B含量增加先减小后增大;当B含量达到x=0.15时,样品中开始有杂相析出。少量B(x=0.05)添加时,合金的饱和磁致伸缩有所提高;随B含量继续增加,合金中形成1:3相以及富硼相,饱和磁致伸缩急剧下降。; 陈先艳马天宇许盼盼严密; 关键词：磁致伸缩 LAVES相

离轴磁场退火后Tb_(0.3)Dy_(0.7)Fe_(1.95)〈110〉取向晶体的磁致伸缩“跳跃”效应被引量：3: 2011年; 将〈110〉取向Tb0.3Dy0.7Fe1.95合金棒放在与轴向成35°夹角的外磁场中退火处理,研究其在0—30MPa预压应力σpre作用下的磁致伸缩效应.结果表明,σpre=0条件下的饱和磁致伸缩值λs由退火前的1023×10-6提高到1650×10-6;σpre≤20MPa范围内,磁场退火后的样品均表现出显著的磁致伸缩"跳跃"效应,并且λs以及跳跃过程完成的磁致伸缩量λm都明显提高.当σpre=20MPa时,λs可达2315×10-6.此外,当σpre≤5MPa时,发生磁致伸缩"跳跃"效应的临界磁场Hjump也较未处理样品有所降低.通过分析磁致伸缩跳跃的临界场、非180°畴变的分布宽度等随σpre的变化规律,揭示了磁场退火前后样品磁化过程的差异.采用磁力显微镜观察了磁场退火前后的磁畴形貌,并探讨了磁场退火感生的各向异性对磁致伸缩性能的影响机理.; 张昌盛马天宇严密; 关键词：磁致伸缩磁场退火

Nd^(3+)对烧结Nd-Fe-B化学镀Ni-P合金结合力和耐蚀性的影响被引量：2: 2009年; 在化学镀液中添加Nd3+,研究其浓度对Ni-P镀层与烧结Nd-Fe-B磁体的结合力和施镀后磁体耐蚀性的影响。测定添加不同浓度Nd3+镀液中所得Ni-P镀层与磁体的结合力,以及镀层在3.5%NaCl(质量分数,下同)溶液中的极化曲线,并结合中性盐雾实验表征施镀后磁体耐蚀性。结果表明,添加2.5g·L-1Nd3+时,Ni-P镀层与Nd-Fe-B磁体的结合力从6.4MPa提高至25.2MPa;施镀后磁体的自腐蚀电位从–0.382V升高到–0.148V,自腐蚀电流密度从4.52μA·cm-2降低到0.07μA·cm-2,耐盐雾腐蚀时间达到256h,磁体耐蚀性显著提高。; 吴元騄罗伟严密; 关键词：烧结ND-FE-B磁体化学镀 NI-P镀层结合力耐蚀性