The surface of an up-conversion luminescence material was modified by overcoating with SiOa, which was synthesized from a hydrolysis progress of telraethoxysilane （TEOS） in alkalescent condition. By analyzing the hydrolyzed mechanism of TEOS, it was found that there was not only physical adsorption but also chemical bonding between the up-conversion material and SiO2. At the same time, some adsorption bands at 1100, 475, 950, and 3500 cm^-1 were found by FI-IR, which were the characteristic bands of Si-OH and Si-O-Si. By analyzing the surface elements of the coated material by XPS, it was found that its surface only included Si, O, and C elements, and not F and Y. In the picture of XRD, there was no additional peak after surface modification, suggesting that the silica shell was amorphous. The small peak at 20 = 23° in the X-ray diffraction pattern of the coated material was caused by the amorphous SiO2 shell, and the TEM image also proved that the surface of the material was successfully modified by overcoating with SiO2. The amount of hydroxyls was then increased on the surface of the material, which made it easy to connect with other active groups.
CUI LiliLIU JieminFAN HuiliXU XiaoweiYANG MinXIAO Junping
A new method was reported for surface modification of an up-conversion luminescence material with hydrosulfide group. The factors that may influence the surface modification,such as reaction time,amount of catalyzer and modifier,and reaction solvent,were investigated. The optimal conditions were that the reaction time,the quantity of the basic catalyzer,the quantity of modifier and the volume of reaction solvent were 40 min,1.0,1.0,and 40 mL,respectively. The results indicated that hydrosulfide group content modified on the surface of up-conversion luminescence material reached to 0.1430 mmol/g,and this modified up-conversion luminescence material could be widely used in the study of structure of protein and the property of microenvironment.
Surface modification of up-conversion luminescence materials （Na[Y0.57Yb0.39Er0.04]F4 modified by amino groups） by grafting and modifying with aldehyde groups was studied by means of Fourier transform infrared spectroscopy （FTIR）, scanning electron microscopy （SEM）, thermogravimetric analysis （TGA）, and emission spectrum （EM）. The surface modification effect was compared using two different finishhag agents, p-phthalaldehyde and glutaraldehyde. It was found that the surface of up-conversion luminescence materials could be modified by aldehyde groups of the two finishing agents, the systematic dispersibility and the thermostability of the up-conversion luminescence material modified by p-phthalaldehyde were better than those of the material modified by glutaraldehyde, and the luminous intensity of the material modified by p-phthalaldehyde was increased. The AI （the ratio of the suspended segmental quality in the specimen to the total mass of the specimen） of the material modified by p-phthalaldehyde was higher than that of the material modified by glutaraldehyde. It is obviously seen that the embellishment effect of p-phthalaldehyde as a finishing agent was better than that of glutaraldehyde. In addition, the reasons why p-phthalaldehyde is a good finishing agent are also explained.