In this paper, Fe30Pt70/Fe3O4 core/shell nanoparticles were synthesized by chemical routine and the layered polyethylenimine （PEI）-Fe30Pt70/Fe3O4 structure was constructed by molecule-mediated self-assembly technique. The dimension of core/shell structured nanoparticles was that of 4nm core and 2 nm shell. After annealing under a flow of forming gas （50%Ar2＋30%H2） for 1 h at or above 400℃, the iron oxide shell was reduced to Fe and diffused to Pt-rieh core, which leaded to the formation of L1. phase FePt at low temperature. The x-ray diffraction results and magnetic properties measurement showed that the chemical ordering temperature of Fe30Pt70/Fe3O4 core/shell nanoparticles assembly can be reduced to as low as 400℃. The sample annealed at 400℃ showed the eoereivity of 4KOe with the applied field of 1.5T. The core/shell structure was suggested to be an effective way to reduce the ordering temperature obviously.