Shot peening can improve fatigue strength of materials by creating compressive residual stress field in their surface layers,and offers a protection against crack initiation and propagation,corrosion,etc.And fatigue fracture and stress corrosion cracking of NAK80 steel parts are improved effectively.Currently there lacks in-depth research in which the beneficial effect of the residual stress may be offset by the surface damage associated with shot peening,especially in terms of the research on the effective control of shot peening intensity.In order to obtain the surface residual stress field of NAK80 steel after shot peening,the samples are shot peened by pneumatic shot peening machine with different rules.The residual stress in the precipitation-hardening layer of NAK80 steel is measured before and after a shot peening treatment by X-ray diffraction method.In order to obtain true residual stress field,integral compensation method is used to correct results.By setting up analytical model of the residual stress in the process of shot peening,the surface residual stress is calculated after shot peening,and mentioning the reason of errors occurred between calculated and experimental residual stresses,which is mainly caused by the measurement error of the shoot arc height.At the same time,micro hardness,microstructure and roughness in the precipitation-hardening layer of NAK80 steel before and after shot peening were measured and surveyed in order to obtain the relation between shot peening strength and surface quality in the precipitation-hardening layer.The results show that the surface quality of NAK80 steel is significantly improved by shot peening process.The over peening effect is produced when the shot peening intensity is too high,it is disadvantageous to improve sample＇s surface integrity,and leading to reduce the fatigue life.When arc high value of optimal shot peening is 0.40 mm,the surface quality is the best,and the depth of residual stress in the precipitation-hardening layer reaches to about 450 μm
Warm tensile tests for aluminum alloy 7022 sheet are held at different temperatures and strain rates. The range of temperature is 293-773 K and that of the strain rate is 0. 001-0.1 s^-1. The warm tensile properties,relations among temperature,strain rate,and the flow stress are discussed. Constitutive equations under the warm tension are obtained based on revised Hooke law and Grosman equation. It is concluded that flow stress declines with the increase of the temperature and the decrease of the strain rates. The elongation percentage increases with the increase of the temperature and the decrease of strain rate.