A simple method for the controllable hydrothermal synthesis of nanocrystalline anatase TiO2(nc-TiO2) particles involving the selection of suitable organic alkali peptizing agents is reported.A dye-sensitized solar cell(DSSC) with square-like nc-TiO2 particles with side lengths about 8-13 nm-prepared using tetraethylammonium hydroxide(TEAOH)-in the photoelectrode showed higher photovoltaic performance than two other DSSCs with square-like nc-TiO2 particles with side lengths about 7-10 nm-prepared using tetrabutylammonium hydroxide-or elongated nc-TiO2 particles with lengths about 18-35 nm and width about 10 18 nm-prepared using tetramethylammonium hydroxide(TMAOH)-in the photoelectrodes.When a scattering layer prepared from sub-micron size spheres or cone-like nc-TiO2 particles-synthesized using a higher concentration of TMAOH-was added on top of the photoelectrode fabricated from nc-TiO2 synthesized with TEAOH,the energy conversion efficiency of the DSSC was markedly increased from 6.77% to 8.18%.