The present study dealt with investigations on the effects of annealing on the hydrogen storage properties of La 1.6 Ti 0.4 MgNi 9 alloys.The experimental alloys were prepared by magnetic levitation melting followed by annealing treatment.For La 1.6 Ti 0.4 MgNi 9 alloys,LaNi 5,LaNi 3 and LaMg 2 Ni 9 were the main phases,Ti 2 Ni phase appeared at 900℃.Annealing not only enhanced the maximum and effective hydrogen storage capacity,improved the hydrogen absorption/desorption kinetics,but also increased the discharge capacity.The cyclic stability had been improved markedly by annealing,e.g.,when the discharge capacity reduced to 60% of maximum discharge capacity,the charge/discharge cycles increased from 66（as-cast） to 89（annealed at 800℃） and 127 times（annealed at 900℃）.La 1.6 Ti 0.4 MgNi 9 alloy annealed at 900℃ exhibited better electrochemical properties compared to the other two alloy electrodes.
The La0.55Pr0.05Nd0.15Mg0.25Ni3.5（Co0.5Al0.5）x（x=0.0, 0.1, 0.3, 0.5） alloys were prepared by magnetic levitation melting under an Ar atmosphere, and the effects of Co and Al on the hydrogen storage and electrochemical properties were systematically investigated by pressure composition isotherms, cyclic voltammetry, Tafel polarization and electrochemical impedance spectroscopy testing. The results showed that the alloy phases were mainly consisted of （La,Pr）（Ni,Co）5, LaMg2Ni9, （La,Nd）2Ni7 and LaNi3 phases, and the cell volumes of （La,Pr）（Ni,Co）5, LaMg2Ni9, （La,Nd）2Ni7 and LaNi3 phases expanded with Co and Al element added. The hydrogen storage capacity initially increased from 1.36 （x=0） to 1.47 wt.% （x=0.3） and then decreased to 1.22 wt.% （x=0.5）. The discharge capacity retention and cycle stability of the alloy electrodes were improved with the increase of Co and Al contents. The La0.55Pr0.05Nd0.15Mg0.25Ni3.5（Co0.5Al0.5）0.3 alloy electrode possessed better electrochemical kinetic characteristic.