The effect of solution temperature and cooling rate on microstructure and mechanical properties of laser solid forming (LSF) Ti-6A1-4V alloy is investigated. The samples are solutions treated at 900, 950, and 1000 ℃, followed by water quenching, air cooling, and furnace cooling, respectively. It is found that the cooling rate of solution treatment hasα more important effect on the microstructure in comparison with the solution temperature. The martensite α formed during water quenching results in the higher hardness and tensile strength but lower ductility of samples. With decreasing the cooling rate and increasing the solution temperature, the width of primary α laths increases, and the aspect ratio and volume fraction decrease, which make the hardness and tensile strength decrease and the ductility increase.
The effects of heat treatment on the microstructure and mechanical properties of laser solid forming (LSF) Ti-6Al-4V alloy were investigated The influences of the temperature and time of solution treatment and aging treatment were analyzed. The results show that the microstructure of LSFed samples consists of Widmanstatten α laths and a little acicular in columnar prior β grains with an average grain width of 300 μm, which grow epitaxiaUy from the substrate along the deposition direction (27). Solution treatment had an important effect on the width, aspect ratio, and volmne fraction of primary and secondary a laths, and aging treatment mainly affects the aspect ratio and volume fraction of primary α laths and the width and volume fraction of secondary a laths. Globular a phase was first observed in LSFed samples when the samples were heat treated with solution treatment (950℃, 8 h/air cooling (AC)) or with solution treatment (950℃, 1 h/AC) and aging treatment (550℃, above 8 h/AC), respectively. The coarsening and globularization mechanisms of a phase in LSFed Ti-6Al-4V alloy during heat treatment were presented. To obtain good integrated mechanical properties for LSFed Ti-6Al-4V alloys, an optimized heat treatment regimen was suggested.
Several tensile samples were prepared using laser rapid forming (LRF) with Ti-6Al-4V alloy as powder material, and the samples were annealed. The microstructure and high temperature mechanical properties of laser formed Ti-6Al-4V alloy through annealing treatment were investigated. The short-term and long-term tensile tests at 350℃were performed. The results show that the microstructure of LRF samples consists of the large columnar priorβgrains which grow epitaxially from the substrate along the deposition direction. There are Widmanstatten a laths in priorβgrains, but a laths in annealed microstructure are coarser, and their aspect ratio is lower than that in as-deposited microstructure. In addition, the priorβgrain boundary is also coarsened and broken off through the annealing treatment. The high temperature mechanical properties of the annealed LRF samples exceed those of casting alloy significantly, especially the stress-rupture lifetime reaches 661.7 h even while the test stress increases from initial value of 490 MPa to the final stress of 800 MPa gradually.
Nickel-based superalloy Rene88DT,has been laser-deposited using laser rapid forming (LRF) route.The mechanical properties and microstructure characteristics of LRF Rene88DT at 25℃ and 750℃ were evaluated.The results shows that both strength and ductility of LRF Rene88DT can be improved significantly by the integration of optimized heat treatment (solution treatment (1160℃,2h/AC) + aging (760℃,8h/AC)) and the HIP treatment(1160℃,2h/200MPa).25℃ tensile properties is comparable to that of the Powder Metallurgy standard.The 750℃ tensile strength and ductility are also comparable to those of the Powder Metallurgy standard,but the yield strength is still a little lower at 750℃.As compared with the as-deposited state,g' precipitates of LRF Rene88DT are evolved gradually to be spherical in shape and uniformly distribute in the g matrix after optimized heat treatment and HIP treatment.Fracture surface shows that crack initiates at the edge for all the samples of LRF Rene88DT after tensile deformation.The deformation is found to be homogeneous in the whole sample.Necking phenomenon exists near the fracture surface,which corresponds with the superior strength and ductility of LRF Rene88DT.
Zhao Xiaoming1,2,Gong Shuili1,Lin Xin2,Chen Jing 2,Huang Weidong21Science and Technology on Power Beam Processes Laboratory,AVIC Beijing Aeronautical Manufacturing Technology Research In-stitute,Beijing 100024,China2State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi’an 710072,China