Mg-9Gd-3Y-1.5Zn-0.8Zr alloys own high strength,good heat and corrosion resistance.However,it is difficult for the fabrication of large-scale billets,due to the poor deformation ability and strong hot-crack tendency.This work investigated the casting process on the microstructures and flow stress behaviors of the semi-continuous casting billets for the fabrication of large-scale Mg-9Gd-3Y-1.5Zn-0.8Zr billets.The casting process(electromagnetic intensity and casting speed)shows outstanding effects on the microstructures and flow stress behavior of the billets.The billets with the specific casting process(I=68 A,V=65 mm/min)exhibit uniform microstructures and good deformation uniformity.
Xuan liuQichi LeZhiqiang ZhangLei BaoZhengxing FanJianzhong Cui
The low frequency electromagnetic field was applied during direct chill(DC) semi-continuous casting of the ZK60 magnesium alloy billets. Effects of low frequency electromagnetic field on surface quality, microstructure and hot-tearing tendency of Φ500 mm ZK60 magnesium alloy billets were investigated. The results showed that with the application of the low frequency electromagnetic field, the surface quality of the ZK60 magnesium alloy billets is markedly improved and the depth of cold fold is decreased. The microstructure of the billets is also significantly refined. Besides, the distribution of the grain size is relatively uniform from the billet surface towards its center, where the average grain size is 42 μm at surface and 50 μm at center. It also shows that the hot-tearing tendency of DC semi-continuous casting ZK60 magnesium alloy billets is significantly reduced under low frequency electromagnetic field.
The effect of ultrasonic power and treatment time on degassing of Mg-6Zn-1Ca alloy was studied in this paper. The degassing effect was characterized by measuring densities of ingots. The results show that proper ultrasonic treatment can remove hydrogen from the melt of the Mg-6Zn-1Ca alloy. The ultrasonic degassing effect is closely related to the ultrasonic power density and treatment time. The degassing efficiency increases with an increase in ultrasonic power density when the melt is treated at 690 °C for 120 s, reaching its highest value at 1.2 W·cm-3. When the power density is 1.2 W·cm-3, with an increase in ultrasonic treatment time, the degassing efficiency increases at first, reaches its peak value at 120 s, then decreases as the ultrasonic treatment is further prolonged. In this experiment, the optimum degassing effect with an efficiency of 67.5 % is obtained by ultrasonic treatment with the power density of 1.2 W·cm-3 for 120 s. The maximum density of ingot can be increased from 1.8069 g·cm-3 to 1.8146 g·cm-3(increased by 0.43%).
Zheng JiaWen-ming ZhangFu YangZhi-qiang ZhangQi-chi LeJian-zhong Cui