Ti45Zr30Ni25 and Ti45Zr30Ni25La alloys were prepared by melt-spinning, and the phase structure and electrochemical performances of the melt-spun alloys were investigated. The results showed that the Ti45Zr30Ni25 alloy was composed of the quasicrystalline phase, amorphous phase and Laves phase. The Ti45Zr30Ni25La alloy contained quasicrystalline and amorphous phases. The maximum discharge capacity was 111 mAh/g for the Ti45Zr30Ni25 alloy electrode, and 124 mAh/g for the Ti45Zr30Ni25La alloy electrode. The Ti45Zr30Ni25La alloy electrode exhibited a better high-rate dischargeability and cycling stability than the Ti45Zr30Ni25 alloy electrode. The improvement of electrochemical properties was mainly ascribed to the increase in the amorphous phase due to the addition of La.
LIU BaozhongWANG LiboZHANG ZhiWU YaomingWANG Limin
Ti44Zr32Ni22Cu2 and Ti41Zr29Ni28Cu2 alloys were prepared by the melt-spinning method. The phase structure was analyzed by X-ray diffraction,and the electrochemical performances of the melt-spun alloys were investigated. The results indicated that the Ti44Zr32Ni22Cu2 alloy was composed of the icosahedral quasicrystals and amorphous phases,and the Ti41Zr29Ni28Cu2 alloy comprised icosahedral quasicrystals,amorphous,and Laves phases. The maximum discharge capacity was 141 mAh/g for the Ti44Zr32Ni22Cu2 alloy and 181 mAh/g for the Ti41Zr29Ni28Cu2 alloy,respectively. The Ti41Zr29Ni28Cu2 alloy also showed a better high-rate dischargeability and cycling stability. The better electrochemical properties should be ascribed to the high content of Ni,which was beneficial to the electrochemical kinetic properties and made the alloy more resistant to oxidation,as well as to the Laves phase in the Ti41Zr29Ni28Cu2 alloy,which could work as the electro-catalyst and the micro-current collector.