Efficient Mode-locked and Q-switched Nd∶YVO_4 Laser with Semiconductor Saturable Absorber Mirror: 2007年; We reported an efficient diode pumped Nd∶YVO4 1 064 nm laser passively mode-locked and Q-switched by a semiconductor saturable absorber mirror(SESAM). At the incident pump power of 7.5 W, 2.81 W average output power was obtained during stable CW mode locking with a repetition rate of 111 MHz. The optical conversion efficiency was 37.5%, and the slope efficiency was 39%. So far as we know, this is the highest optical-optical conversion efficiency with a SESAM at home.; LIU Shi-huaHONG Zheng-pingWANG Chun-huiWANG Guang-gangLI LeiLIU Shu-shanLIU MinLIU JieWANG Yong-gangQIN Lian-jie; 关键词：MODE-LOCKED

溶胶-凝胶法制备Li-N双掺p型ZnO薄膜的结构、光学和电学性能被引量：14: 2010年; 采用溶胶-凝胶法在n型Si(100)衬底上沉积Li-N双掺杂ZnO薄膜,经X射线衍射和扫描电镜图片分析,所制备薄膜具有多晶纤锌矿结构和高的c轴择优取向.室温下霍尔效应测试结果显示Li-N双掺杂ZnO薄膜具有p型导电特性.在Li掺杂量为15.0at%,Li/N(摩尔比)为1∶1,700℃退火等优化条件下得到的最佳电学性能结果是:电阻率为0.34Ω.cm,霍尔迁移率为16.43cm2/V.s,载流子浓度为2.79×1019cm-3.另外,室温下光致发光谱显示,所制备样品具有较强的近紫外和紫光发射,而可见光区范围内与缺陷相关的深能级发射则较微弱.本文还就掺杂浓度和退火温度对薄膜的结构、光学性能以及电学性能的影响进行了讨论.; 王德义高书霞李刚赵鸣; 关键词：P型ZNO薄膜溶胶-凝胶

LD泵浦Nd∶YVO_4/SESAM锁模激光器实验研究被引量：3: 2008年; 报道了利用LD泵浦Nd∶YVO4激光器,用半导体可饱和吸收镜(SESAM)做被动锁模元件,实现了高效的连续锁模运转,输入功率7.5W时得到2.45W的激光输出,光-光转换效率达32.7%,锁模脉冲的重复频率为108MHz。; 刘士华王广刚王春慧李雷刘树山刘敏刘杰秦连杰; 关键词：二极管激光器 ND:YVO4 被动锁模 SESAM

Yb_(0.03)Y_(0.19)Gd_(0.78)VO_4晶体的生长和性能被引量：1: 2008年; 液相合成了Yb∶YGdVO4多晶料,采用中频感应加热Czochralski法生长了Yb0.03Y0.19Gd0.78VO4晶体。用浮力法测定其密度为5.29g/cm3,X射线粉末衍射分析表明它的结构与YVO4和GdVO4的晶体结构相同,并计算出了它的晶胞参数为a0=b0=0.7191nm,c0=0.6329nm。用激光脉冲法测量了晶体的热扩散系数,比较了晶体a轴和c轴的热扩散系数随温度的变化关系。实验表明Yb0.03Y0.19Gd0.78VO4晶体有希望适合作为LD泵浦的激光晶体材料。; 秦连杰李兵帅张溶姜付义王波; 关键词：晶体生长热扩散系数

退火温度对溶胶-凝胶法制备Na掺杂ZnO薄膜的结构和光学特性的影响被引量：12: 2009年; 采用溶胶-凝胶旋涂法在Si(100)衬底上制备Na掺杂ZnO薄膜,退火温度分别为873,973,1073K。研究了退火温度对Na掺杂ZnO薄膜形貌、微观结构和光学性能的影响。室温光致发光谱显示,在973K下退火的样品具有中心位于361nm处尖锐而强的紫外发光峰,在388,425nm处各有一个比较弱的紫色和蓝色发光峰,在可见光范围内发光峰的强度很弱。; 高书霞王德义; 关键词：微结构光学特性溶胶-凝胶法