Mn0.1Ce0.9Ox and Mn0.1Ce0.6Zr0.30x samples synthesized by sol-gel method were tested for redox properties through the dynamic oxygen storage measurement and characterized using X-ray diffraction, BET, electron paramagnetic resonance, and X-ray photoelectron spectroscopy. The results showed that redox performances of ceria-based materials could be enhanced by synergetic effects between Mn-O and Ce-O. Fresh and aged samples were characterized with the fluorite-type cubic structure similar to CeO2, and furthermore, the thermal stability of Mn0.1Ce0.9Ox materials was improved by the introduction of some Zr atoms. From XPS, it could be concluded that Mn^2＋/Mn^3＋ redox couples existed on the surface of Mn0.1Ce0.9Ox and Mn0.1Ce0.6Zr0.3Ox samples. Electron paramagnetic resonance researches revealed that there were three types of Mn^2＋ species： isolated Mn^2＋ substituting for Ce^4＋ ions in the lattice with a cubic symmetry, ones in defect with a noncubic symmetry, and at the surface of samples.
The durability of three-way catalyst （TWC） and corresponding close-coupled catalyst （CCC） for Euro Ⅳ stage regulation was investigated through Vehicle Road Running Mode tests, whereas emissions of regulated pollutants of three car fleet were investigated at every 100,000 km miles. The results showed that HC, NOx, and CO emission values could meet Euro Ⅳ regulation limits at every point. The redox properties of TWC and CCC were measured by CO reduction during each isothermal. It was obvious that both aged TWC and aged CCC behaved a good redox property at 673 and 773 K. Based on XRD and BET measurement results, TWC and CCC washcoat were characterized with good thermal stability.