A novel membrane distillation concentration method was used m prepare high concentration polyaluminum chloride （PAC1） with high content of AID or Ale. 2.52 mol/L PACl1 with 88% Alb and 2.38 mol/L PACl2 with 61% Ale were successfully prepared. Three coagulants, AlCl3, PACl1 and PACl2 were investigated on their hydrolysis behavior and speciation under different conditions. The effects of pH and dilution ratio on Al species distribution were investigated by ferron assay. Experimental result showed that pH had a significant effect on Al species distribution for the three coagulants. Dilution ratio had little effects on Alb and Alc distribution in whole dilution process except the beginning for PACl1 and PACl2. The results indicated that transformation of Al depends largely on their original composition. AlCl3 was the most unstable coagulant among these three coagulants during hydrolysis process. PACl1 and PACl2 with significant amounts of highly charged and stable polynuclear aluminum hydrolysis products were less affected by the hydrolysis conditions and could maintain high speciation stability under various conditions.
Worldwide environment has resulted in a limit on the sulfur content of gasoline.It is urgent to investigate the desulfurization of gasoline.The polydimethylsiloxane(PDMS)/polyetherimide(PEI)composite membranes were prepared by casting a PDMS solution onto porous PEI substrates and characterized by scanning electron microscope(SEM).The membranes were used for sulfur removal from gasoline by pervaporation.The effects of feed temperature,sulfur content in the feed and PDMS layer thickness on membrane performance were investigated,and an activation energy of permeation was obtained.Experimental results indicated that higher feed temperature yielded higher total flux and lower sulfur enrichment factor.The total flux varied little with the increase of sulfur content in the feed,but the sulfur enrichment factor first increased with the amount of thiophene added into the gasoline,and then the variation was little.The increase of PDMS layer thickness resulted in a smaller flux but a larger sulfur enrichment factor.The result indicates that the PDMS/PEI composite membranes are promising for desulfurization by pervaporation.