In this work,the effect of dioctadecyl dimethyl ammonium chloride（DDAC,a kind of alkyl ammonium salt） on polar β phase content and the diameter of electrospun PVDF nanofibers was investigated for the first time.Our experimental results show that the diameter of the electrospun PVDF nanofiber could be largely reduced and the content of polar β phase also become dominant immediately by just adding a little amount of DDAC.When the mass fraction of DDAC reached 4%,the content of polar β phase increased by about 39.1% compared with PVDF nanofibers without DDAC.Besides,the crystallinity of PVDF nanofibers also increased with the addition of DDAC.Based on the results,the possible mechanism of cooperative effect between electrospinning and DDAC on fiber diameter and formation of β phase in PVDF was discussed.
Modified castor oil-based epoxy resin （EP）/polyurethane （PU） grafted copolymer by glycidyl polyhedral oligomeric silsesquioxane （glycidyl POSS） was synthesized. The damping properties, thermal stability, mechanical properties and morphology of the grafted copolymer modified by glycidyl POSS were studied systematically. The results revealed that the incorporation of glycidyl POSS improved the damping performance evidently and broadened damping temperature range, especially when the glycidyl POSS content was 0.2%-1%. At the same time, there was a slight increase in thermal stability with the increase of POSS content. The tensile properties changed with the change of the copolymer＇s Tg, decreased at low POSS contents and increased at high POSS contents. This modified copolymer has the potential to be used as film damping material or constrained damping layer.
Abstract In the field of polymer/graphene nanocomposites, massive production and commercial availability of graphene are essential. Exfoliation of graphite to obtain graphene is one of the most promising ways to large-scale production at extremely low cost. In this work we illustrate a facile strategy for mass production of few-layered （≤ 10） graphene （FLG） via the newly explored ball milling. The achieved FLG concentration was determined by UV/Vis spectroscopy. The formation of FLG was proved by measuring the flake thickness by atomic force microscopy （AFM）. Further Raman spectral studies indicated that the crystal structure of exfoliated flakes was preserved satisfactorily during this shear-force dominating process. To increase the maximum concentration obtainable, it＇s critical to make a good parameter assessment. N-methylpyrrolidone （NMP） was used as a dispersing medium and the effect of milling parameters was systematically and quantitatively investigated, thus providing a criterion to optimize the milling process. We established the optimal values for solvent volume and initial weight of graphite. As for milling time, the production of FLG was enhanced with continuous milling according to the power law, but not linearly with increasing milling time. Moreover, the possible mechanism involved in milling process was also explored. Our work provides a simple method for graphite exfoliation and has great potential for improving thermal and electrical conductivity of polymer composites in the fields of engineering.
In this work, hybrid conductive fillers of carbon black （CB） and carbon nanotubes （CNTs） were introduced into polylactide （PLA）/thermoplastic poly（ether）urethane （TPU） blend （70/30 by weight） to tune the phase morphology and realize rapid electrically actuated shape memory effect （SME）. Particularly, the dispersion of conductive fillers, the phase morphology, the electrical conductivities and the shape memory properties of the composites containing CB or CB/CNTs were comparatively investigated. The results suggested that both CB and CNTs were selectively localized in TPU phase, and induced the morphological change from the sea-island structure to the co-continuous structure. The presence of CNTs resulted in a denser CB/CNTs network, which enhanced the continuity of TPU phase. Because the formed continuous TPU phase provided stronger recovery driving force, the PLA/TPU/CB/CNTs composites showed better shape recovery properties compared with the PLA/TPU/CB composites at the same CB content. Moreover, the CB and CNTs exerted a synergistic effect on enhancing the electrical conduetivities of the composites. As a result, the prepared composites exhibited excellent electrically actuated SME and the shape recovery speed was also greatly enhanced. This work demonstrated a promising strategy to achieve rapid electrically actuated SME via the addition of hybrid nanoparticles with self-networking ability in binary PLA/TPU blends over a much larger composition range.