The microstructures and free-volume evolutions of as-cast and pre-annealed Zr65Al7.5Ni10Cu12.5Ag5 bulk metallic glasses during rolling deformation have been investigated. No phase transformation is detected in the as-cast/rolled specimen. However,the structural stability of the glass against plastic deformation is worse after pre-annealing,indicated by nanocrystallization in preannealed/rolled specimens with large deformation degrees. Moreover,with increasing deformation degree,the free-volume content in a pre-annealed/rolled specimen increases at a lower average rate than that in an as-cast/rolled specimen.
ZHOU Wei LU BinFeng KONG LingTi LI JinFu ZHOU YaoHe
Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） rods were abraded to different surface roughnesses using different types of waterproof abrasive papers and sometimes polishing pastes, and the compressive deformation behavior was examined. The results show that the yield strength of the BMG is hardly affected while the compressive plasticity increases from 2.3% to 4.5% with decreasing the surface roughness. Observation of the fractured samples under a scanning electron microscope indicates that the rise in plasticity is accompanied with an increase in shear band density. The results suggest that it is necessary to reduce the surface roughness of BMGs for achieving a large plasticity.